(1) Background: Erosive lesions of dental enamel are steadily increasing owing to both the availability of exogenous acid and the production of endogenous acid. The aim of this study was to investigate the erosion-inhibiting potential of a diode laser irradiation and topical application of fluoride used alone or in combination on the enamel surface of extracted teeth before exposure to an acidic solution. (2) Methods: The four axial enamel surfaces of 40 healthy molars were used for four study groups: (A) no treatment; (B) application of fluoride gel for 120 s; (O) a diode laser application for 120 s; and (X) a combined laser/fluoride for 120 s. Each enamel surface was examined by SEM (scanning electron microscopy). (3) Results: At 700× magnification, it was possible to detect the enamel prisms of the test area of groups A, B, and O, while no structures such as enamel prisms were highlighted for group X because they were covered by an amorphous layer. The mean number of prisms ×1000 µm2 was 7.2 units with an SD of 0.72 for group A, 8 units with an SD of 0.96 for group B, and 4.8 units with a SD of 0.4 for group O. Student’s t-test showed no significant difference between group A and B with a p = 0.054. Group O showed a significant reduction of prims ×1000 µm2 compared with group A (p = 0.0027) and group B (p = 0.0009). Student’s t-test showed no significant difference between groups A and B with a p = 0.054. Group O showed a significant reduction of prims density with respect to group A (p = 0.0027) and group B (p = 0.0009). (4) Conclusions: This amorphous layer might be correlated with the effect of laser on enamel, which reduces both water and carbonate ion; increases the crystallinity of hydroxyapatite, and improves the mechanical properties of enamel; which is responsible for greater protection expressed by the enamel of group X against acid attacks.

Enamel Erosion Reduction through Coupled Sodium Fluoride and Laser Treatments before Exposition in an Acid Environment: An In Vitro Randomized Control SEM Morphometric Analysis

Femiano F.
;
Femiano R.;Santaniello M.;Grassia V.;Aversa R.;Apicella A.
;
2022

Abstract

(1) Background: Erosive lesions of dental enamel are steadily increasing owing to both the availability of exogenous acid and the production of endogenous acid. The aim of this study was to investigate the erosion-inhibiting potential of a diode laser irradiation and topical application of fluoride used alone or in combination on the enamel surface of extracted teeth before exposure to an acidic solution. (2) Methods: The four axial enamel surfaces of 40 healthy molars were used for four study groups: (A) no treatment; (B) application of fluoride gel for 120 s; (O) a diode laser application for 120 s; and (X) a combined laser/fluoride for 120 s. Each enamel surface was examined by SEM (scanning electron microscopy). (3) Results: At 700× magnification, it was possible to detect the enamel prisms of the test area of groups A, B, and O, while no structures such as enamel prisms were highlighted for group X because they were covered by an amorphous layer. The mean number of prisms ×1000 µm2 was 7.2 units with an SD of 0.72 for group A, 8 units with an SD of 0.96 for group B, and 4.8 units with a SD of 0.4 for group O. Student’s t-test showed no significant difference between group A and B with a p = 0.054. Group O showed a significant reduction of prims ×1000 µm2 compared with group A (p = 0.0027) and group B (p = 0.0009). Student’s t-test showed no significant difference between groups A and B with a p = 0.054. Group O showed a significant reduction of prims density with respect to group A (p = 0.0027) and group B (p = 0.0009). (4) Conclusions: This amorphous layer might be correlated with the effect of laser on enamel, which reduces both water and carbonate ion; increases the crystallinity of hydroxyapatite, and improves the mechanical properties of enamel; which is responsible for greater protection expressed by the enamel of group X against acid attacks.
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11591/466317
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 3
  • ???jsp.display-item.citation.isi??? ND
social impact