YBa(2)Cu(3)O(7-delta) (YBCO) grain boundaries characterized by a misalignment of the c-axes (45 degrees c-axis tilt or 45 degrees c-axis twist) have been obtained by employing a recently implemented biepitaxial technique. Junctions based on these grain boundaries exhibit good Josephson properties useful for applications. High values of the I(C)R(N) product and a Fraunhofer-like dependence of the critical current on the magnetic field, differently from traditional biepitaxial junctions, have been obtained. The correlation between transport properties and microstructure has been investigated by Transmission Electron Microscopy (TEM), which was also performed on previously measured junctions. The presence of atomically clean basal plane (BP) faced tilt boundaries, among other types of interfaces, has been shown. The possibility of selecting these kinds of boundaries by controlling film growth, and their possible advantages in terms of reproducibility and uniformity of the junction properties an discussed. The possibility of employing these junctions to explore the symmetry of the order parameter is also discussed.
Josephson phenomenology and microstructure of YBa2Cu3O7-x artificial grain boundaries characterized by misalignment of the c-axes
TAFURI, Francesco;
1999
Abstract
YBa(2)Cu(3)O(7-delta) (YBCO) grain boundaries characterized by a misalignment of the c-axes (45 degrees c-axis tilt or 45 degrees c-axis twist) have been obtained by employing a recently implemented biepitaxial technique. Junctions based on these grain boundaries exhibit good Josephson properties useful for applications. High values of the I(C)R(N) product and a Fraunhofer-like dependence of the critical current on the magnetic field, differently from traditional biepitaxial junctions, have been obtained. The correlation between transport properties and microstructure has been investigated by Transmission Electron Microscopy (TEM), which was also performed on previously measured junctions. The presence of atomically clean basal plane (BP) faced tilt boundaries, among other types of interfaces, has been shown. The possibility of selecting these kinds of boundaries by controlling film growth, and their possible advantages in terms of reproducibility and uniformity of the junction properties an discussed. The possibility of employing these junctions to explore the symmetry of the order parameter is also discussed.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.