IRIS è la soluzione IT che facilita la raccolta e la gestione dei dati relativi alle attività e ai prodotti della ricerca. Fornisce a ricercatori, amministratori e valutatori gli strumenti per monitorare i risultati della ricerca, aumentarne la visibilità e allocare in modo efficace le risorse disponibili.
EnglishYBaCuO nanowires were reproducibly fabricated down to widths of 50 nm. A Au/Ti cap layer on YBCO yielded high electrical performance up to temperatures above 80 K in single nanowires. Critical current density of tens of MA cm2 at T D 4:2 K and of 10 MA cm2 at 77 K were achieved that survive in high magnetic fields. Phase-slip processes were tuned by choosing the size of the nanochannels and the intensity of the applied external magnetic field. Data indicate that YBCO nanowires are a rather attractive system for the fabrication of efficient sensors, supporting the notion of futuristic THz devices
| Titolo: | High critical-current density and scaling of phase-slip processes in YBaCuO nanowires |
| Autori: | |
| Data di pubblicazione: | 2012 |
| Rivista: | |
| Abstract: | YBaCuO nanowires were reproducibly fabricated down to widths of 50 nm. A Au/Ti cap layer on YBCO yielded high electrical performance up to temperatures above 80 K in single nanowires. Critical current density of tens of MA cm2 at T D 4:2 K and of 10 MA cm2 at 77 K were achieved that survive in high magnetic fields. Phase-slip processes were tuned by choosing the size of the nanochannels and the intensity of the applied external magnetic field. Data indicate that YBCO nanowires are a rather attractive system for the fabrication of efficient sensors, supporting the notion of futuristic THz devices |
| Handle: | http://hdl.handle.net/11591/189955 |
| Appare nelle tipologie: | 1.1 Articolo in rivista |
File in questo prodotto:
http://hdl.handle.net/11591/189955
Copyright © 2021